① Dvije cifre na početku broja čelika označavaju sadržaj ugljika u čeliku, izražen kao nekoliko desetina hiljada prosječnog sadržaja ugljika, kao što je 40Cr.
②Glavni legirajući elementi u čeliku, osim nekoliko mikrolegirajućih elemenata, općenito su izraženi u procentima. Kada je prosječan sadržaj legure<1.5%, the steel number is generally marked with the element symbol instead of the content. However, in special cases where confusion is likely to occur, the number "1" can also be marked after the element symbol, such as the steel number. "12CrMoV" and "12Cr1MoV", the former has a chromium content of 0.4-0.6%, the latter has a chromium content of 0.9-1.2%, and the rest of the ingredients are the same. When the average content of alloy elements is ≥1.5%, ≥2.5%, ≥3.5%..., the content should be indicated after the element symbol, which can be expressed as 2, 3, 4... etc. accordingly. For example 18Cr2Ni4WA.
③Legirajući elementi kao što su vanadij V, titanijum Ti, aluminijum AL, bor B i retke zemlje RE u čeliku su svi elementi mikrolegiranja. Iako je sadržaj vrlo nizak, ipak ih treba označiti u klasi čelika. Na primjer, u 20MnVB čeliku. Vanadijum je 0.07-0.12%, a bor 0.001-0.005%.
④Visokokvalitetni čelik treba dodati "A" na kraju broja čelika kako bi se razlikovao od općenitog visokokvalitetnog čelika.
⑤ Legirani konstrukcioni čelik specijalne namjene, broju čelika prethodi (ili ima sufiks) simbol koji predstavlja svrhu tipa čelika. Na primjer, čelik 30CrMnSi koji se posebno koristi za zakovice, broj čelika je izražen kao ML30CrMnSi.
Cijevi od legure i bešavne cijevi su i srodne i različite i ne mogu se zamijeniti.
Legirane cijevi su čelične cijevi definirane prema materijalima koji se koriste za proizvodnju (tj. materijalima). Kao što ime govori, to su cijevi od legure; dok su bešavne cijevi čelične cijevi definirane prema proizvodnom procesu (bešavne i bešavne). Razlika od bešavnih cijevi je u šavnim cijevima, uključujući cijevi sa ravnim šavom i spiralne cijevi.